316L zanglamaydigan po'latdan yasalgan tasma
Asosiy ma'lumotlar
316L zanglamaydigan po'latdan yasalgan tasma texnik xususiyatlari
Darajasi: 316 L
Standart: ASTM/EN/JIS
Qalinligi: 0,03 mm-3,0 mm
Kengligi: 1,5 mm-600 mm
Uzunlik: lasan turi yoki mijozning talabiga binoan ishlab chiqarilishi mumkin
Yuzaki pardozlash: NO.1, 2B, 2H (Rerolled Bright), BA, №4, 8K (oyna), HL (Soch chizig'i), Polishing Bright va boshqalar
Chet: Tegirmon qirrasi, Yoriq qirrasi, Debured qirrasi, Dumaloq qirrasi, V tipidagi chekka
316L zanglamaydigan po'latdan yasalgan tasma afzalliklari
Korroziyaga qarshilik
316L zanglamaydigan po'latdan yasalgan chiziqning korroziyaga chidamliligi 304 zanglamaydigan po'latdan yasalgan chiziqdan yaxshiroqdir va pulpa va qog'oz sanoati ishlab chiqarish jarayonida yaxshi korroziyaga chidamliligiga ega.Va 316L zanglamaydigan po'latdan yasalgan chiziq okeanning eroziyasiga va korroziy sanoat atmosferasiga ham chidamli.
Issiqlikka chidamlilik
1600 darajadan past bo'lgan intervalgacha dasturda 316 zanglamaydigan po'latdan yasalgan chiziq yaxshi oksidlanish qarshiligiga ega.
316L zanglamaydigan po'latdan yasalgan chiziq oddiy 316 zanglamaydigan po'latdan ko'ra karbid yog'inlariga nisbatan yaxshi qarshilikka ega.
Tavsif
| Turi | Baho | Baho | Kimyoviy komponent % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Boshqa | |||
| Ostenitik | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3.50-5.50 | 5,50-7,50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | - | ||
| 301 | 1.431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1.4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304 l | 1.4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304H | 1.4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1.4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1.4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1.4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316 l | 1.4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Ti | 1.4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 317 l | 1.4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1.455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| 347H | 1.494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronik50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1,00 | - | 0,2-0,4 | Nb: 0,10-0,30 V: 0,10-0,30 | |
| 904 l | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1,00 | 0.1 | Cu: 1,0-2,0 | |||
| Ikki tomonlama | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1,00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21,5-24,5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1,00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1.446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1,00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferrit | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1,00 | - | ≤0,25 | - | |
| Martensit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | 0,75 | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3.50-5.50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Zanglamaydigan po'latdan yasalgan plitalar darajasi Baogu ta'minoti
| Yuzaki ishlov berish | Xususiyatlari va qo'llanilishi |
| 2B | 2B ning sirt yorqinligi va tekisligi no2D dan yaxshiroqdir.keyin mexanik xususiyatlarini yaxshilash uchun maxsus sirt ishlov berish orqali No2B keng qamrovli foydalanishni deyarli qondirishi mumkin. |
| №1 | №100-#200 qirrali abraziv kamar bilan sayqallangan, to'xtovsiz qo'pol chiziqlar bilan yanada yorqinroq bo'lib, qurilish, elektr jihozlari va oshxona anjomlari va boshqalar uchun ichki va tashqi bezak sifatida ishlatiladi. |
| №4 | №150-#180 qirrali abraziv kamar bilan sayqallangan, uzluksiz qo'pol chiziqlar bilan yaxshi yorqinlikka ega, lekin №3 dan yupqaroq, vannaxona binolarining ichki va tashqi bezaklarida elektr jihozlari, oshxona anjomlari va oziq-ovqat mahsulotlarini qayta ishlash uskunalari va boshqalar sifatida ishlatiladi. |
| HL | №4 qoplamada № 150-# 320 qirrali abraziv kamar bilan sayqallangan va doimiy chiziqlarga ega bo'lib, asosan binolarning bezaklari liftlari, bino eshigi, old plastinka va boshqalar sifatida ishlatiladi. |
| BA | Sovuq haddelenmiş, yorqin tavlangan va teridan o'tgan mahsulot ajoyib yorqinlik va oyna, oshxona jihozlari, bezak va boshqalar kabi yaxshi refleksga ega. |
| 8K | Mahsulot ajoyib yorqinlikka ega va ko'zgu bo'lish uchun reflektorlikni afzal ko'radi. |